A team of researchers recently published a paper in the journal Materials that demonstrated the effects of boron (B) doping on graphite interlayer spacing. Graphite Lined Crucible
Study: Effect of Boron Doping on the Interlayer Spacing of Graphite . Image Credit: Miriam Doerr Martin Frommherz/Shutterstock.com
Boron (B) is used extensively as a graphitization catalyst in the synthesis of carbonaceous materials used in lithium-ion (Li-ion) battery anodes as it can improve the graphitization degree and reduce the graphitization temperature.
Boron carbide (B4C) clusters are formed when B atoms are inserted into graphite. Additionally, several B atoms can replace the carbon atoms in the graphite since the atomic radius of B is similar to that of carbon, which significantly influences the physicochemical properties, electrochemical performance, and structure of the graphite.
B1s XPS spectra of the boron-doped graphite studied. (a) Boron-doped graphite prepared using needle coke (GC) as raw material; (b) Boron-doped graphite prepared using pitch coke (PIC) as raw material. Image Credit: Bao, C et al., Materials
The reduction in the interlayer spacing is a major structural characteristic of B-doped carbon materials such as graphite. Several studies have demonstrated that B-doped graphite possesses a smaller interlayer spacing compared to ideal graphite.
The substitutional B atoms (sub-B) in the graphite lattice and dissolution–precipitation of carbon atoms are responsible for the decrease in the interlayer spacing. The carbon dissolution–precipitation mechanism is attributed to the exceptional catalytic effects of B, which accelerates the homogeneous graphitization of graphite in a gradual manner. However, the interlayer spacing is increased when the B atoms occupy the interstitial positions in the lattice.
The factors responsible for the smaller interlayer spacing in the B-doped graphite compared to virgin graphite have not been identified until now. However, two mechanisms were considered to understand the effects of sub-B on the graphite interlayer spacing.
The first mechanism was based on the depleted p-electrons between the graphitic layers after B doping which leads to a lower Π-electron density within the graphite layers due to the higher valence state of carbon compared to B and a shorter interlayer distance. The second mechanism was based on the Poisson contraction along the c-axis owing to the expansion along the a-axis. However, these mechanisms were not verified experimentally.
In this study, researchers synthesized B-doped graphite using B4C powder as a graphitization catalyst through the heat treatment of coke and systematically investigated the sub-B content variation in the carbon lattice after the addition of B4C catalyst and the effects of sub-B atoms on the graphite interlayer spacing.
Pitch coke, needle coke, and B4C powder were used as the starting materials. Initially, needle coke/pitch coke was homogenously mixed with B4C powder and transferred in a graphite crucible placed in the medium-frequency induction graphitizing furnace center.
The furnace was flushed and evacuated with argon gas three times to eliminate moisture and oxygen. The temperature of the furnace was increased to 2700 °C at a 10 °C/min heating rate, and the coke-B4C mixture was annealed under an argon atmosphere for 2 h.
9%, 6%, 3%, and 0% B4C powder was mixed with the needle coke/pitch coke to synthesize eight B-doped graphite samples. The samples synthesized using needle coke were designated as 9GC27, 6GC27, 3GC27, and 0GC27, while the samples synthesized using pitch coke were designated as 9PIC27, 6PIC27, 3PIC27, and 0PIC27 based on their B4C powder concentration.
(a,b) two boron-doped graphite models, in which the pink atoms are boron and the grey atoms are carbon; E is the total energy of the models after optimization of the geometry. Image Credit: Bao, C et al., Materials
X-ray photoelectron spectroscopy (XPS) was used to characterize the synthesized samples. The interlayer spacing of the synthesized B-doped graphite samples was measured using the X-ray diffraction (XRD) method and the Bragg equation.
The DMol3 package of Materials Studio was used to perform all density functional theory (DFT) calculations. The interactions formed between the ions and electrons were described using the Linear combination of atomic orbitals. Total energies were calculated by performing Brillouin zone integrations.
The double-numeric quality basis set with polarization functions and the Perdew–Burke–Ernzerhof (PBE) model under the generalized gradient approximation were used to evaluate the electron exchange-correlation interactions.
A periodic B-doped graphite supercell structure was established to understand the sub-B-induced interlayer spacing reduction mechanism. The B mass ratio was set at 1.78% based on the experimental results Two types of B-doped graphite models were optimized and the DFT calculations of the Poisson’s ratio, electrostatic surface potential, total charge density, Mulliken partial charges, and partial density of states were performed on these structures.
Researchers successfully synthesized B-doped graphite using coke and B4C powder, utilizing the heat treatment method. B-atoms were effectively incorporated into the graphite lattice during heat treatment, leading to a reduction in the graphite interlayer spacing.
The interlayer spacing decreased with the increasing concentration of B atoms in the B-doped graphite lattice. The interlayer spacing values achieved in 9PIC27 and 9GC27 were 0.33537 nm and 0.33545 nm, respectively, which was close to the interlayer spacing value of 0.3354 nm of ideal graphite.
The B doping increased the number of sub-B atoms in the graphite lattice, which broke the electron balance between carbon layers and facilitated the transfer of electrons in small amounts from an adjacent B atom free layer to a B atom containing layer.
Charge density diagram within the (010) plane of (a) graphite and (b) boron-doped graphite across the boron atoms. Carbon: dark grey, boron: pink. Image Credit: Bao, C et al., Materials
Both the B atom containing layer and its adjacent carbon layer were in an electron-deficient state due to the electron-deficient nature of B atoms and electron transfer from the carbon layer to the B atom containing layer, which increased the electrostatic surface potential of the carbon layers and decreased electron repulsion between the layers.
The attractive forces between the carbon layers and Π electrons in the adjacent layer and the decrease in the Π electron repulsion forces between the carbon layers also played a significant role in decreasing the interlayer spacing.
Taken together, the findings of this study demonstrated that the electron redistribution induced by B doping played the most crucial role in reducing the interlayer spacing in B-doped graphite.
Bao, C., Zeng, Q., Li, F. et al. Effect of Boron Doping on the Interlayer Spacing of Graphite. Materials 2022. https://www.mdpi.com/1996-1944/15/12/4203
Disclaimer: The views expressed here are those of the author expressed in their private capacity and do not necessarily represent the views of AZoM.com Limited T/A AZoNetwork the owner and operator of this website. This disclaimer forms part of the Terms and conditions of use of this website.
Samudrapom Dam is a freelance scientific and business writer based in Kolkata, India. He has been writing articles related to business and scientific topics for more than one and a half years. He has extensive experience in writing about advanced technologies, information technology, machinery, metals and metal products, clean technologies, finance and banking, automotive, household products, and the aerospace industry. He is passionate about the latest developments in advanced technologies, the ways these developments can be implemented in a real-world situation, and how these developments can positively impact common people.
Please use one of the following formats to cite this article in your essay, paper or report:
Dam, Samudrapom. (2022, June 16). Impact of Boron Doping on the Interlayer Spacing of Graphite. AZoM. Retrieved on December 29, 2022 from https://www.azom.com/news.aspx?newsID=59343.
Dam, Samudrapom. "Impact of Boron Doping on the Interlayer Spacing of Graphite". AZoM. 29 December 2022. <https://www.azom.com/news.aspx?newsID=59343>.
Dam, Samudrapom. "Impact of Boron Doping on the Interlayer Spacing of Graphite". AZoM. https://www.azom.com/news.aspx?newsID=59343. (accessed December 29, 2022).
Dam, Samudrapom. 2022. Impact of Boron Doping on the Interlayer Spacing of Graphite. AZoM, viewed 29 December 2022, https://www.azom.com/news.aspx?newsID=59343.
Do you have a review, update or anything you would like to add to this news story?
In this interview, AZoM speaks with Beau Preston, Founder of Rainscreen Consulting, about STRONGIRT, an ideal continuous insulation (CI) cladding attachment support system and its applications.
AZoM speaks with Dr. Shenlong Zhao and Bin-Wei Zhang about their new research that is focused on realizing high-performance room-temperature sodium-sulfur batteries as an alternative to lithium-ion batteries.
In AZoM's latest interview, we talk with Jeff Shainline from the NIST in Boulder, CO, about his research looking at forming superconducting circuits with synaptic behavior. This research could transform how we approach AI and computing.
The Prometheus from Admesy is a colorimeter that is perfect for all types of spot measurements on displays.
This product profile outlines the ZEISS Sigma FE-SEM for high-quality imaging and advanced analytical microscopy.
The SB254 provides high performance electron-beam lithography at a cost-effective rate. It enables the handling of various compound semiconductor materials.
The global semiconductor market has entered an exciting period. Demand for chip technology is both driving the industry as well as hindering it, with current chip shortages predicted to last for some time. Current trends will likely shape the future of the industry, which is set to continue to show
The primary distinction between graphene-based batteries and solid-state batteries lies in the composition of either electrode. Although the cathode is commonly changed, carbon allotropes can also be employed in fabricating anodes.
In recent years, the IoT is rapidly being introduced into almost all sectors, but it has particular importance in the EV industry.
AZoM.com - An AZoNetwork Site
Natural Flake Graphite Owned and operated by AZoNetwork, © 2000-2022